SJH103 Acetic Slicone Sealant | ||||||
Performance | standard | Measureed value | Testing Method | |||
Test at 50±5% RH and temperature 23±2ºC | ||||||
Density (g/cm3) | ±0.1 | 0.96 | GB/T13477 | |||
Tack-free time(min) | ≤180 | 10 | GB/T13477 | |||
Extrusion(ml/min) | ≥80 | 750 | GB/T13477 | |||
Tensile Modulus (Mpa) | 23ºC | 0.4 | 0.1-0.46 | GB/T13477 | ||
20ºC | 0.6 | 0.1-0.7 | ||||
Slumpability(mm) vertical | Not change shape | Not change shape | GB/T13477 | |||
Slumpability (mm) horizontal | ≤3 | 0 | GB/T13477 | |||
Curing speed(mm/d) | 2 | 2 | ||||
As cured-after 21 days at 50±5% RH and temperature 23±2ºC | ||||||
Hardness (shore A) | 20-60 | 26 | GB/T531 | |||
Tensile strength under standard conditions (mpa) | 0.29 | GB/T13477 | ||||
Elongation of ruputue(%) | 478.6 | GB/T13477 | ||||
Movement capability(%) | 12.5 | 12.3 | GB/T13477 | |||
stroage | 12 months |